OWN - Quintessenz Verlags-GmbH CI - Copyright Quintessenz Verlags-GmbH OCI - Copyright Quintessenz Verlags-GmbH TA - Int J Prosthodont JT - The International Journal of Prosthodontics IS - 1942-4426 (Electronic) IS - 0893-2174 (Print) IP - 3 VI - 34 PST - ppublish DP - 2021 PG - 357-364 LA - en TI - Repair of Aged Polymer-Based CAD/CAM Ceramics Treated with Different Bonding Protocols FAU - Bayazıt, Elif Öztürk AU - Bayazıt E CN - AB - Purpose: The aim of this study was to compare the microtensile bond strength (μTBS) of different CAD/CAM polymer-based ceramics to a repair composite resin using various bonding protocols. Materials and Methods: Three different CAD/CAM polymer-based ceramics (LAVA Ultimate [LU], 3M ESPE; VITA Enamic [VE], VITA Zahnfabrik; and CeraSmart [CS], GC) were used. Ceramic slices were obtained and subjected to thermal cycling between 5°C and 55°C for 5,000 cycles with a 30-second dwell time. The samples were randomly separated into the following groups: universal adhesive (UB); hydrofluoric acid (HF); sandblasting (SN); HF + UB; HF + ceramic primer (PR) + adhesive (GB); SN + UB; and SN + PR + GB. The repair composite resin (G-aenial Universal Flo, GC) was applied to the samples and subjected to re-aging between 5°C and 55°C for an additional 5,000 cycles. Parallel sections were removed from the specimens, and multiple beamshaped micro sticks (1.0 mm × 1.0 mm × 10 mm) were prepared for each group. Subsequently, the μTBS test was performed, and the obtained data were statistically analyzed via one- and two-way analysis of variance and Tukey post hoc tests. Scanning electron microscopy (SEM) analysis was also performed. Results: Significant differences were found among the experimental groups (P < .05). The μTBS values of the UB bond groups were higher than those with the GB bond. The effect of pretreatment on μTBS (ηP 2 = 0.556) was more significant than ceramic type (ηP 2 = 0.481), and this result was supported by the SEM images. Conclusion: Pretreatment before application of universal adhesive is still needed to repair hybrid ceramic restorations with composite resins. AID - 1213443