PMID- 23534013 OWN - Quintessenz Verlags-GmbH CI - Copyright Quintessenz Verlags-GmbH OCI - Copyright Quintessenz Verlags-GmbH TA - J Adhes Dent JT - The Journal of Adhesive Dentistry IS - 1757-9988 (Electronic) IP - 4 VI - 15 PST - ppublish DP - 2013 PG - 361-368 LA - en TI - Effect of Resin Cement Type on the Microtensile Bond Strength to Lithium Disilicate Ceramic and Dentin Using Different Test Assemblies LID - 10.3290/j.jad.a28624 [doi] FAU - Marocho, Susana María Salazar AU - Marocho S FAU - Özcan, Mutlu AU - Özcan M FAU - Amaral, Regina AU - Amaral R FAU - Bottino, Marco Antonio AU - Bottino M FAU - Valandro, Luiz Felipe AU - Valandro L CN - OT - adhesion OT - aging OT - bond strength OT - ceramic OT - dentin OT - lithium disilicate OT - microtensile bond strength AB - Purpose: This study evaluated the microtensile bond strength (µTBS) of 3 different resin cements to lithium-disilicate ceramic using two assemblies: ceramic-cement-ceramic (CCC) and ceramic-cement-dentin (CCD). Materials and Methods: The bonding surfaces of lithium disilicate ceramic blocks (5 × 5 × 4 mm) (Nblock = 90) were etched with 4% hydrofluoric acid for 20 s and silanized. Flat dentin surfaces of human third molars were conditioned according to the respective manufacturer's specifications for three types of resin cements (ML: Multilink, Ivoclar-Vivadent; PF: Panavia F, Kuraray; SB: Super Bond C&B, Sun Medical). While one set of ceramic blocks (n = 30) was cemented to another equal set (CCC assembly), another set of ceramic blocks (n = 30) was cemented on flat dentin (CCD assembly). The bonded specimens were stored in distilled water at 37°C for 24 h, and then sectioned along the x- and y-axes to obtain nontrimmed beam specimens. The beam specimens were randomly divided into two conditions: dry condition (DC - immediate testing); and aging condition (AC - thermocycling 12,000 times + water storage for 150 days). The µTBS bond strength test was performed using a universal testing machine (1 mm/min). After debonding, the substrate and adherent surfaces were analyzed using a scanning electron microscope to categorize the failure types. The data were statistically evaluated using 2-way ANOVA and Tukey's test (5%). Results: While the mean µTBS of CCC assemblies were significantly influenced by the cement type (p < 0.05) and aging (p < 0.05), CCD assemblies showed a significant effect of the cement (p < 0.05) but not the aging (p > 0.05). Without aging (DC), the mean µTBS (MPa) of SB (26.9) and PF (26.9) were significantly higher than ML (18.5) (p < 0.05). For CCC after aging (AC), SB (26.6) showed higher mean µTBS than those of PF (16.4) and ML (18.5) (p < 0.05). However, in CCD after AC, no significant difference was found between the groups (p > 0.05). In both CCC and CCD assemblies, pre-test failures were the least with SB cement. Regardless of the resin cement type employed and storage conditions, adhesive failures ranged between 35.3% and 88.9%, cohesive failures in cement between 2.3% and 35.3%, and cohesive failures in ceramic between 3.3% and 6.8%. Conclusion: SB resin cement demonstrated the highest bond strength to a lithium disilicate ceramic in both tests assemblies with and without aging conditions. AID - 843064